Product Details
1. Products Description
Micro grain raw material
Grain size: 0.4-0.6μm
Co 10%, 12%
TRS >3600 N/mm2
Hardness HRA 91.8-92.5
Work piece HRC45-50 HRC55-60 HRC65 HRC68
Helix angle 30°-45 °
Diameter of cutting edge 0.2-0.9 mm; 1-20 mm
Diameter of rods 4-20 mm
Length 50-100 mm
Cutting Form Flat, Square, Ball nose, Corner Radius, Taper Flute, etc
Flutes No. 1-7
HRC45 |
HRC55 |
HRC60 |
HRC65 |
Grain Size:0.6um Co:10 % Flexural strength:3350N/mm2 |
Grain Size:0.6um Co:10 % Flexural strength:4000N/mm2 |
Grain Size:0.5um Co:12 % Flexural strength:4300N/mm2 |
Grain Size:0.4um Co:12.5 % Flexural strength:4300N/mm2 |
2. Application
Used for cutting Carbon steel, Tool steel, Mould steel, Stainless steel, Titanium alloy, Copper, Cast Iron and Aluminium, etc.
Grinding equipment: WALTER, ANCA, ROLLOMATIC
Testing equipment: ZOLLER
3. Coating
Coating
|
Color
|
Coating Temperature
|
Thickness (um)
|
HV
|
Application Temperature
|
Friction coefficient
|
TiAlN
|
Purple-Gray |
<600°C |
3-5 |
3300 |
800 °C |
0.3 |
AlTiN |
Black |
<600 °C |
3-5 |
3500 |
900 °C |
0.3 |
TiSiN |
Copper |
<600 °C |
3-5 |
3500 |
1500 °C |
0.4 |
NaNo |
Blue |
<600 °C |
3-5 |
3800 |
1200 °C |
0.4 |
CrN |
Silver Gray |
<480 °C |
2-2.5 |
2500 |
700 °C |
0.3 |
4. PackingBrand Laser printed on cutter shank, 1 pcs in a plastic tube, 10 pcs a group
5. Delivery timeKeep stock for regular types
Samples: 3 - 5 days
Regular orders: 7 - 10 days